Influence of the oxygen/argon ratio on the properties of sputtered hafnium oxide

In this work we have focused our attention on the role of the gas mixture (O2/Ar) used during HfO2 thin film processing by r.f. magnetron sputtering, to produce dielectrics with suitable characteristics to be used as gate dielectric. Increasing the O2/Ar ratio from 0 to 0.2, the films properties (optical gap, permittivity, resistivity and compactness) are improved. At these conditions, films with a band gap around 5 eV were produced, indicating a good stoichiometry. Also the flat band voltage has a reduction of almost three times indicating also a reduction of the same order on the fixed charge density at the semiconductor–insulator interface. The dielectric constant is around 16 which is very good, since the surface of the silicon where the HfO2 films were deposited contains a SiO2 layer of about 3 nm that gives an effective dielectric constant above 20, close to the HfO2 stoichiometric value (∼25). Further increase on the O2/Ar ratio does not produce significant improvements.