Effect of pre-treatment on recrystallization and recrystallization textures of cold rolled CC AA 5182 aluminum alloy

The effect of pre-treatment on recrystallization and recrystallization textures of cold rolled continuous cast (CC) AA 5182 aluminum alloy as well as on the earing behavior was investigated. The progress of recrystallization was tracked by means of measurements of tensile properties. The texture of cold rolled and annealed samples was determined by X-ray diffraction. The results show that the recrystallization temperature of cold rolled CC AA 5182 aluminum alloy without pre-treatment is about 24 °C higher than that of the alloy with pre-treatment. The recrystallization textures of cold rolled CC AA 5182 aluminum alloy are characterized by the R, cube and Goss orientations. The recrystallization textures of cold rolled CC AA 5182 aluminum alloy without pre-treatment exhibit stronger cube and Goss components and a weaker R component than those of the alloy with pre-treatment. The deformed and recovered samples without pre-treatment possess a significantly higher 45° earing than the samples with pre-treatment, while the recrystallized samples without pre-treatment possess a slightly lower 45° earing than the samples with pre-treatment.