Evolution of photo-stimulated luminescence of EB-PVD/(Ni, Pt)Al thermal barrier coatings

Experiments are described which were designed to assess the suitability of photo-stimulated luminescence piezo-spectroscopy (PLPS) measurements as a basis for non-destructive inspection (NDI) and determination of life remaining of thermal barrier coatings (TBCs). Thermal cyclic tests were conducted on 7 wt.% Y2O3 stabilized ZrO2 (YSZ) electron beam physical vapor deposited (EB-PVD)/(Ni, Pt)Al/CMSX-4 TBCs at two temperatures 1151 and 1121 °C. The evolution of PLPS spectral characteristics (peak frequency shift, peak width and area ratio of peaks) was studied as a function of thermal cycles. It was observed that the average thermally grown oxide (TGO) stress and its standard deviation, and the area ratio of peaks show systematic change with thermal cycling, indicating that these characteristics can be used for NDI and determination of life remaining. The average TGO stress increases initially and then decreases monotonically with thermal cycling. The rate of change in the stress can be related to specimen life: the shallower the slope, the higher the life. The peak area ratio also decreases monotonically with cycling. The average TGO stress changes in a systematic manner versus remaining life fraction independent of temperature. Remaining life predictions were made based on average stress versus life fraction, which resulted in life assessments within ±13% of actual values excluding one specimen with abnormal behavior.