Enhancement of the piezoelectric properties of sodium lanthanum bismuth titanate (Na0.5La0.5Bi4Ti4O15) through modification with cobalt

The dielectric, piezoelectric, and electromechanical properties of B-site cobalt-modified sodium lanthanum bismuth titanate (Na0.5La0.5Bi4Ti4O15, NLBT) piezoelectric ceramics were investigated. The piezoelectric properties of NLBT ceramics can be enhanced by cobalt modifications. The NLBT ceramics modified with 0.2 wt.% cobalt trioxide (NLBT-C4) possess good piezoelectric properties, with piezoelectric coefficient d33 of 27 pC/N, electromechanical coupling factors (kp and kt) of 6.5% and 28.5%, and mechanical quality factor Qm (kp mode) of 3400. The Curie temperature Tc of cobalt-modified NLBT ceramics was found to slightly higher than that of pure NLBT ceramics. A large dielectric abnormity in dielectric loss tan δ was observed in NLBT ceramics, which can be significantly suppressed by cobalt modification. Thermal annealing studies presented the cobalt-modified NLBT ceramics possess stable piezoelectric properties.