Bainite transformation and TRIP effect in 20Mn2SiVB steel

Transformation-induced plasticity (TRIP) steel is a relatively new type of automotive steel known for its combination of high-strength and high ductility which was developed in the 1990s. 20Mn2SiVB steel is a kind of TRIP steel with low-carbon and low-alloying contents and high-strength. Specimens of a tested 20Mn2SiVB steel austenitized at 920 °C and austempered at 420 °C in a salt bath at different time are investigated. The microstructure obtained is studied by means of optical microscopy, scanning electron microscopy and X-ray diffraction. The results show that bainitic ferrite precipitates at the boundary of the austenite first, and with the prolongation of the isothermal time, the amount of bainitic ferrite increase. Then the ferrite decollates the austenite grain and lath-shaped bainitic ferrite with little island-shaped austenite forms during the holding time. The microstructure contains carbide-free bainite, granular bainite, retained austenite and martensite in the process of bainite transformation. Tensile test of the different treated specimens indicates that a better comprehensive property can be gained after austenized at 920 °C following austempered at 420 °C for 5 min, a certain TRIP effect can be also obtained under this condition.