Stress corrosion cracking of API X-60 pipeline in a soil containing water
Author/Authors
Pan، نويسنده , , B.W. and Peng، نويسنده , , X. and Chu، نويسنده , , W.Y. and Su، نويسنده , , Y.J. and Qiao، نويسنده , , L.J.، نويسنده ,
Issue Information
روزنامه با شماره پیاپی سال 2006
Pages
6
From page
76
To page
81
Abstract
Stress corrosion cracking (SCC) of a API X-60 pipeline steel in a soil containing 33% water has been investigated using slow strain rate tests and sustained load test of single-edge cracked sample. The results showed that a transgranular SCC in the soil occurred when ε ˙ ≤ 3.5 × 10 − 7 s − 1 , and the susceptibility to SCC was about 30%. SCC of the cracked sample in the soil at sustained load could also occur, and the threshold stress intensity factor of SCC was KISCC = 0.73KC.
Keywords
API X-60 pipeline , Stress corrosion cracking , Corrosion-induced stress , Soil containing water
Journal title
MATERIALS SCIENCE & ENGINEERING: A
Serial Year
2006
Journal title
MATERIALS SCIENCE & ENGINEERING: A
Record number
2150237
Link To Document