Effects of SrTiO3 on dielectric and piezoelectric properties of K0.48Na0.48Li0.04Nb0.96Ta0.04O3-based piezoceramics

In this study, (100 − x) K0.48Na0.48Li0.04Nb0.96Ta0.04O3 − xSrTiO3 (0 ≤ x ≤ 10) ceramics were fabricated via normal sintering of synthesized powder by using solid state reaction. All ceramics revealed pure perovskite structure, indicating formation of solid solution between KNNLT and ST up to 10%. With increasing x, the crystal structure of ceramics changed from orthorhombic to tetragonal and finally pseudocubic symmetry when x = 10. Ceramic containing 1% ST had orthorhombic and tetragonal symmetries, simultaneously. Investigation of the variation of dielectric constant of ceramics versus temperature revealed that for ceramic with x = 1, polymorphic phase transition (PPT) temperature between orthorhombic and tetragonal is less than room temperature. Thus coexistence of two different structures in this ceramic is due to vicinity of its composition to morphotropic phase boundary (MPB). As a result, the maximum piezoelectric constant was measured for this ceramic. Ceramics containing 5 and 7.5% ST tend to appear relaxor ferroelectric behavior which is because of chemical inhomogeneities in both A- and B-sites of the ABO3 perovskite structure.