Microstructure and mechanical properties of molybdenum silicides with Al additions

Several molybdenum silicides alloys with different aluminum additions were produced by the arc-cast method. Microstructure observed in the alloys presented a variation of the precipitated second phase respect to the aluminum content. Evaluation of the compressive behavior at high temperature of the alloys shows an important improvement in its ductility, approximately of 20%. Fracture toughness was increased proportionally with Al content. In addition at room temperature the alloys show a better mechanical behavior in comparison with the sample unalloyed. In general, Al additions result to be a good alternative to improve the resistance of these intermetallic alloys. The results are interpreted on the base of the analysis of second phase strengthening.