Microstructures and mechanical properties of pure copper deformed severely by equal-channel angular pressing and high pressure torsion

Pure Cu of 99.98 wt.% purity has been processed at room temperature by diverse techniques of severe plastic deformation, namely equal-channel angular pressing (ECAP), high pressure torsion (HPT) and a combination of both in order to find out the evolution on the microstructural homogeneity for each of the processes and their combination. Starting with a grain size of ∼60 μm, severe plastic deformation has been introduced to the material while maintaining the sample dimensions unchanged through the processes of ECAP and HPT. A significant decrease in grain size was observed by transmission electronic microscopy (TEM). Microtensile and microhardness tests were carried out on the deformed material in the three processing conditions. A significant improvement of the tensile strength was promoted with admissible penalization on ductility.