Effect of Mg and Sr-modification on the mechanical properties of 319-type aluminum cast alloys subjected to artificial aging

Aluminum-based 319-type cast alloys are commonly used in the automotive industry to manufacture cylinder heads and engine blocks. These applications require good mechanical properties and in order to achieve them through precipitation hardening, artificial aging treatments are applied to the products. The standard artificial aging treatment for alloy 319, as defined by the T6 heat treatment temper, consists in solution heat-treating the product for 8 h at 495 °C, water quenching at 60 °C, and then artificially aging at 155 °C for 2–5 h. esent paper reports on aging heat treatments that were performed on four Al–Si–Cu–Mg 319-type alloys: 319 base alloy, Sr-modified 319 alloy, 319 alloy containing 0.4 wt% Mg, and the Sr-modified 319 + 0.4 wt% Mg alloy. This investigation was carried out in order to examine the effect of Sr-modification and additions of Mg on the microhardness, tensile strength and impact properties of 319-type alloys over a range of aging temperatures and times (150–240 °C, for periods of 2–8 h). sults show that the best combination of properties is found in the Sr-modified alloy containing 0.4 wt% Mg (i.e. alloy 319 + Mg + Sr). Also, the optimum artificial aging temperature changes when Mg is present in the alloy.