Residual stresses in surface induction hardening of steels: Comparison between experiment and simulation

Deep induction hardening has been performed on two batches of smooth cylindrical specimens with a hardening depth respectively around 2 mm and 3 mm. The distributions of axial and circumferential residual stresses are analysed for the two specimen batches by X-ray diffraction technique. The radial normal stress field is estimated through the use of the well known Moore and Evans correction. Finally, the experimental residual stresses are compared with those obtained from a multiphysic finite element modelling of the whole induction treatment process, including electromagnetic, thermal, metallurgical and mechanical phenomena. The simulated residual stress field is in good agreement with X-ray analysis especially at depths lower than one-tenth the specimen diameter. At deeper depths, a correction of the experimental X-ray analysis has been done to obtain realistic values.