Effects of peening on mechanical properties in friction stir welded 2195 aluminum alloy joints

The effects of surface treatment techniques like laser and shot peening on the mechanical properties were investigated for friction stir welded 2195 aluminum alloy joints. The loading in the tensile specimens was applied in a direction perpendicular to the weld direction. The peening effects on the local mechanical properties through the different regions of the weld were characterized using a digital image correlation technique assuming an iso-stress condition. This assumption implies that the stress is uniform over the cross-section and is equal to the average stress. The surface strain and average stress were used giving an average stress–strain curve over the region of interest. The extension of the iso-stress assumption to calculate local stress–strain curves in surface treated regions is a novel approach and will help to understand and improve the local behavior at various regions across the weld resulting in a sound welding process. The surface and through-thickness residual stresses were also assessed using the X-ray diffraction and the contour methods. The laser peened samples displayed approximately 60% increase in the yield strength of the material. In contrast, shot peening exhibited only modest improvement to the tensile properties when compared to the unpeened FSW specimens. The result that laser peening is superior to shot peening because of the depth of penetration is original since this superiority has not been presented before regarding mechanical properties performance.