Microstructure and mechanical properties of the accumulative roll bonded (ARBed) pure magnesium sheet

The pure Mg sheets were processed by ARB at 400 °C and 300 °C up to 8 cycles and 4 cycles, respectively. The microstructure was refined during the first cycle and only homogenized during the following ARB process due to the high deformation temperature, intermediate reheating and air-cooling. The ARB process did not show an obvious effect on the tensile properties of the as-ARBed pure Mg sheet due to the stable grain size and dominant basal plane texture during ARB. Further deformation should be introduced to improve the bonding quality of the as-ARBed sheet.