Thermomechanical treatment for enhancing gamma fiber component in recrystallization texture of copper-bearing bake hardening steel

A two-step rolling–annealing process has been developed to increase the 〈1 1 1〉//ND (γ fiber) component in the recrystallization texture of a copper-bearing bake hardening steel. The two step process comprises the first rolling by a low reduction in thickness and subsequent annealing at 780 °C, followed by the second rolling by a high reduction and subsequent annealing at 780 °C. The first rolling process aims at seeding the γ fiber oriented grains, so that they can grow at the expense of differently oriented grains developed in the second rolling process. In this way the density of γ fiber component in the recrystallization texture of the bake hardening steel much increases compared with that in the conventional one-step rolling–annealing process.