Author/Authors :
Roy، نويسنده , , D. and Mitra، نويسنده , , R. and Ojo، نويسنده , , O.A. and Singh، نويسنده , , S.S. and Kolesnikov، نويسنده , , D. and Lojkowski، نويسنده , , W. and Scattergood، نويسنده , , R.O. and Koch، نويسنده , , C.C. and Manna، نويسنده , , I.، نويسنده ,
Abstract :
Mechanically alloyed in situ nano Al3Ti dispersed Al50Ti40Si10 amorphous matrix alloy powder was consolidated by hot isostatic pressing in the temperature range of 300–600 °C with a pressure of 1.2 GPa and holed at this temperature for 10 min. Microstructural and phase evolution studies of the mechanically alloyed powder and sintered compacts were conducted by X-ray diffraction and transmission electron microscopy. Alloy sintered at 500 °C recorded an excellent combination of high hardness (8.61 GPa), compressive strength (1212 MPa) and Youngʹs modulus (149 GPa). Furthermore, these results have been compared with that of earlier studies based on conventional sintering (CCS), and high pressure sintering (HPS).
Keywords :
Nano-structure , mechanical properties , Electron microscopy , Hot Isostatic Pressing