Title of article :
Annealing behavior of nano-crystalline austenitic SUS316L produced by HPT
Author/Authors :
Wang، نويسنده , , Hongcai and Shuro، نويسنده , , Innocent and Umemoto، نويسنده , , Minoru and Ho-Hung، نويسنده , , Kuo and Todaka، نويسنده , , Yoshikazu، نويسنده ,
Issue Information :
روزنامه با شماره پیاپی سال 2012
Abstract :
Nano-crystalline (NC) 316L austenitic stainless steel sample was prepared by means of High Pressure Torsion (HPT) and post-deformation annealing. Uniaxial tensile tests at room temperature showed the nano-crystalline sample exhibits extreme high yield strength up to 2230 MPa, which is the highest ever reported in the literature.
Keywords :
element segregation , Nano-crystalline materials , High pressure torsion , 316L Austenitic stainless steel , G phase precipitation
Journal title :
MATERIALS SCIENCE & ENGINEERING: A
Journal title :
MATERIALS SCIENCE & ENGINEERING: A