Processing and characterization of Al–Cu–Li alloy AA2195 undergoing scale up production through the vacuum induction melting technique

The inherent properties of lithium, such as high reactivity and toxicity, relatively low density, low melting point, along with its high cost requires a special technological approach to cast Al–Cu–Li alloy AA2195 as compared to the conventional Direct Chill (DC) casting of aluminum alloys. This paper describes the processing requirements for melting and casting of 200 kg of Al–Cu–Li alloy in a Vacuum Induction Melting (VIM) furnace under dynamic inert atmosphere. The as-cast billets have been homogenized to remove microsegregation as well as to avoid incipient melting, and subsequently subjected for secondary metal processing operations viz., forging and rolling. The product in the form of 4 mm thick sheets was subjected to various heat treatments in T8 (Solution Treatment+WQ+CW+Aging) condition. Mechanical properties were evaluated at room temperature and were correlated with microstructures of the sheets processed under different conditions using transmission electron microscopy (TEM).