Effect of heat-treatment on microstructure and high-temperature deformation behavior of a low rhenium-containing single crystal nickel-based superalloy

A low rhenium-containing [001] oriented single crystal nickel-based superalloy with different γ′ morphologies induced by various aging treatments was compressed from room temperature to 1000 °C. All the single crystal samples with different γ′ morphologies exhibit anomalous yield behavior. The sample first aged at 1180 °C has the widest anomalous temperature domain and highest yield strengths. The sample first aged at 1000 °C has the highest anomalous peak stress temperature.