Metallographic characterisation of Al6061-T6 aluminium plates subjected to ballistic impact

Al6061-T6 aluminium single layer plates, of different thickness, impacted by two different 7.62 mm Armour Piercing projectiles are studied from a metallographic point of view. The material behaviour after ballistic impact is investigated by optical and scanning electron microscopy as well as by micro-hardness tests. The study allows one to highlight the physical phenomena that happen during the impact: the formation of adiabatic shear bands (ASB), the evolution of softening and hardening phenomena, the creation of petalling, plugging and the formation of a melted film between the target and the penetrator as well as the localised failure mechanism. The thermo-mechanical effects on the target and the penetrator material have been examined in order to investigate in the physical phenomena ruling the ballistic damage; the differences between the two types of impactors are also highlighted. Among interesting findings, it has been noticed that a complete penetration is less detrimental and tungsten core projectile seems more damaging for the structural integrity of Al6061-T6 plates. A complete penetration allows the material to better dissipate the plastic deformation energy induced by bullet whereas the arrest increases localised material softening effect resulting in the formation of ASB. gh the creation of numerical models is not the aim of the present paper, the findings could be useful for the building of a modelling approach capable of replicating all the involved phenomena in details.