Physical properties and microstructure of Ti(CN)-based cermets with different WC particle size

Ti(CN)-based cermets with different WC particle sizes from 0.2 to 4 μm were prepared at 1450 °C with 2 MPa Air pressure. The microstructure of cermets was investigated by scanning electron microscope (SEM), X-ray diffraction (XRD), Transmission electron microscope (TEM). The results showed that all the cermets with different WC particle sizes have a typical “core–rim” structure. With the increase of WC powder sizes, the frequency and portion of Ti(C0.7N0.3) cores and rim are somewhat decreased while the portion of white core is increased, due to the relative dissolution rate decreasing. In addition, the fracture mode of Ti(C,N) based cermets is a mixture of trans-granular (primary) and inter-granular (subordinate) fracture. The TRS (about 1850 MPa) of the cermets fluctuate slightly with the WC particle sizes from 0.2 to 1.0 μm, but decrease evidently with WC particle sizes up to 2 μm.