Microstructure and mechanical properties of newly developed aluminum–lithium alloy 2A97 welded by fiber laser

The newly developed aluminum–lithium alloy 2A97 was for the first time joined by laser beam welding in order to meet the ever-increased long-term requirements of aerospace, aviation and armament industries. The weld appearance, microstructure, solute segregation, precipitate behavior, and their relationships with mechanical properties of welded joints were investigated. Sound joints with no crack and a few small porosities are obtained under appropriate heat inputs. As a result of heterogeneous nucleation involving the effect of Zr and Li, a non-dendritic equiaxed zone forms between partially melted zone and fusion zone. The crystal morphologies in fusion zone vary from columnar dendrite to equiaxed dendrite, with the increase of constitutional supercooling. Solute segregation leads to the variations of Cu content in grain interior and boundary, as well as the weak ability of re-precipitation of fusion zone. Most precipitates in the base metal dissolve during welding, and fusion zone contains a decreased quantity of δ′, β′, θ′, and T1. The ultimate tensile strength of laser welded joints is 83.4% of that of the base metal, and can meet the application requirements from related industries, but the ductility still needs to be improved. Welding defects and loss of solid solution/precipitation hardened structure lead to the degradation of mechanical properties. Tensile fracture occurs in weld with the brittle intergranular dominated mode and premature failure occurs and extends in the equiaxed zone.