Wavelength dependent neutron transmission and radiography investigations of the high temperature behaviour of materials applied in nuclear fuel and control rod claddings

Neutron radiography was used for the investigation of the nuclear fuel and control rod cladding behaviour during steam oxidation under severe nuclear accident conditions. In order to verify the hypothesis that the unexpectedly high neutron cross-section found after oxidation of Zircaloy-4 in wet air containing 10% steam is caused by a strong hydrogen uptake, the wavelength dependence of the total macroscopic neutron cross-section of the specimens was measured. The characteristic dependence for hydrogen was not found, which is a proof that hydrogen is not absorbed significantly. The data agree mostly with the behaviour expected for β-Zr. ations of control rod simulators annealed until the failure in single-rod tests were performed. In order to separate the effect of the neutron absorber and control rod structure materials, radiographs taken with different neutron spectra were combined. This procedure clearly showed that the local melting resulting from the eutectic reaction between the stainless steel control rod cladding and the Zircaloy-4 guide tube is the reason for the failure.