Double-layer effects on the lifetime of newly developed HBC-foils for RCS of J-PARC

We have developed hybrid type boron-mixed carbon (HBC) foils for the rapid cycling synchrotron (RCS) of Japan-proton accelerator research complex (J-PARC) using the controlled DC arc-discharge method. The method has been found suitable for the production of thick foils up to a maximum of 700 μg/cm2 due to the strong adhesion to the substrate. The foils thus produced showed rather long lifetime. development, high-temperature damage (foil deformation, thickness reduction and pinhole formation) of the foil was significantly mitigated even at a temperature of approximately 1700 K. However, when the foil temperature was higher than about 1800 K, especially pinhole formation in the irradiated area of the foil and its peripheries were always observed. In order to relieve high-temperature damage, we investigated the possibility to lower the temperature rise in single and double layer HBC-foils while keeping the total thickness the same. We also compared the lifetime of the single and the double layer HBC-foils as well as diamond and commercially available foils, using a 3.2 MeV Ne+ ion beam from the Van de Graaff accelerator.