Effects of Mo on the Microstructure and Hydrogen Sorption Properties of Ti-Mo Getters

The effects of Mo on the microstructure evolution, porosity and hydrogen sorption properties of Ti-Mo getters are investigated in this work. The results show that the addition of Mo prolongs the densification process of Ti-Mo getters and results in a significant amount of sintered pores. With the Mo content increasing, the porosity of getters firstly increases reaching the maximum value as it attains about 7.5wt.%, and then drops. At the room temperature, the hydrogen sorption property of getters increases progressively with the Mo content increasing, but the tendency is not very clear before its content lies below 2.5wt.%. When the Mo content achieves about 7.5wt.%, the hydrogen sorption property proves to be the best. The discussion is made about the above mentioned phenomena inclusive of hydrogen sorption properties of getters under different activation conditions (from 500–750 °C).