Analysis of wear track and debris of stir cast LM13/Zr composite at elevated temperatures

Particulate reinforced aluminum metal matrix composite is in high demand in automobile industry where the operational conditions vary from low to high temperature. In order to understand the wear mode at elevated temperature, this study was planned. For this purpose we developed a metal matrix composite containing aluminum alloy (LM13) as matrix and zircon sand as particulate reinforcement by stir casting process. Different amounts of zircon sand (5, 10, 15 and 20 wt.%) were incorporated in the matrix to study the effect of reinforcement on the wear resistance. Dispersion of zircon sand particles in the matrix was confirmed by using optical microscopy. Sliding wear tests were done to study the durability of the composite with respect to the base alloy. The effects of load and temperature on wear behavior from room temperature to 300 °C were studied to understand the wear mechanism deeply. Surface morphology of the worn surfaces after the wear tests as well as wear debris was observed under scanning electron microscope. Mild to severe wear transition was noticed in tests at high temperature and high load. However, there is interesting change in wear behavior of the composite near the critical temperature of the composite. All the observed behavior has been explained with reference to the observed microstructure of the wear track and debris.