Oxidation and alpha-case formation in Ti–6Al–2Sn–4Zr–2Mo alloy

Isothermal heat treatments in ambient air were performed on wrought Ti–6Al–2Sn–4Zr–2Mo (Ti-6242) material at 500, 593 and 700°C for times up to 500 h. In the presence of oxygen at elevated temperatures simultaneous reactions occurred in Ti-6242 alloy, which resulted in the formation of an oxide scale and a layer with higher oxygen concentration (termed as alpha-case). Total weight gain analysis showed that there was a transition in the oxidation kinetics. At 500°C, the oxidation kinetics obeyed a cubic relationship up to 200 h and thereafter changed to parabolic at prolonged exposure times. At 593°C, it followed a parabolic relationship. After heat treatment at 700°C, the oxidation obeyed a parabolic relationship up to 200 h and thereafter changed to linear at prolonged exposure times. The observed transition is believed to be due to the differences observed in the oxide scale. The activation energy for parabolic oxidation was estimated to be 157 kJ/mol. In addition, alpha-case layer was evaluated using optical microscope, electron probe micro-analyser and microhardness tester. The thickness of the alpha-case layer was found to be a function of temperature and time, increasing proportionally, and following a parabolic relationship. The activation energy for the formation of alpha-case layer was estimated to be 153 kJ/mol.