Value adding limestone to filler grade through an ultra-fine grinding process in jet mill for use in plastic industries

In this study, ultra-fine grinding of limestone was carried out in jet mill using four levels of classifier rotational speed and grinding pressure. The holdup amount was determined during the grinding process, while the feed rate was kept constant at 8 kg/h. The ground product was characterized for its particle size and shape. In addition, the mechanochemical effect on the ground product was characterized through XRD. The particles size of the ground product ranged from 2.21 μm to 7.29 μm, demonstrating various particle shapes such as cubical, angular, and elongated. The degree of crystallinity of the ground product ranged from 54.5% to 93.7%. Afterwards, the ground product was incorporated as filler in polypropylene (PP), and its performance was characterized for mechanical properties. After conducting the test work, we find that the PP filled with ground limestone exhibited excellent thermal and mechanical properties. The composite flexural modulus, impact strength, tensile strength, and elongation at break were 2.1 GPa, 42 kJ/m2, 22.75 MPa, and 21%, respectively, when loaded up to 20%. It likewise exhibited CTE value of 57.2 ppm/°C.