Combustion of micro aluminum–water mixtures

An experimental investigation on the combustion behavior of micro-sized aluminum (μAl)–water mixtures was conducted. It was easily ignited and self-deflagrated on μAl and liquid water when using a paper shell tube. Linear burning rates of quasi-homogeneous mixtures of μAl and liquid water as a function of pressure, mixture composition, density and environment gas medium were measured. Steady-state burning rates were obtained at room temperature using a windowed vessel for a pressure range of 1–80 bar in a nitrogen atmosphere, particle size of 0.5 × 30 × 30 μm and overall mixture equivalence ratios from 0.67 to 2.0. The pressure exponent was obtained as 0.47 at room temperature and compared to the case of nano-sized aluminum (nAl) and liquid water. When a wire was inserted into the sample, for increasing local heat transfer, burning rates were found to be faster.