Evaluation of crack propagation in dental composites by optical coherence tomography

Objectives rpose of this study was to image the sites of fracture initiation and slow crack propagation in a fiber reinforced composite, using the optical coherence tomography (OCT) technique. s ecimens (2 mm × 3 mm × 25 mm) of fiber reinforced composite were mechanically and thermally cycled to emulate oral conditions. The interior of these samples was analyzed prior to and after loading, using OCT. The device used was a home-built Fourier domain OCT setup working at 800 nm with 6 μm spatial resolution. s specimens after load cycling were analyzed. It was clearly seen that OCT images provide an insight into crack propagation, which is not seen by the naked eye. icance ng OCT the possibility of analyzing the fracture propagation quantitatively, and in depth, was added, opening up possibilities to quantitative studies.