Failure analysis of a hydro-processing reactor
Author/Authors :
Wang، نويسنده , , Yang and Lu، نويسنده , , Ye-Bo and Pan، نويسنده , , Hong-Liang، نويسنده ,
Issue Information :
روزنامه با شماره پیاپی سال 2009
Abstract :
Analyzed is the failure of a stainless steel (SS) hydro-processing reactor that is used for flavor-fragrance test. It is found that the cracks on the reactor wall are typical of stress corrosion cracking caused by chloride from the process catalyst. Recommendations are made to mitigate the aforementioned cracking failure.
Keywords :
Catalyst , chloride , Hydro-processing reactor , Failure analysis , Stress corrosion cracking (SCC)