Numerical stress and crack initiation analysis of the compressor blades after foreign object damage subjected to high-cycle fatigue

This paper presents results of the complex stress and crack initiation analysis of the PZL-10 W turbo-engine compressor blade subjected to high cycle fatigue (HCF). A nonlinear finite element method was utilized to determine the stress state of the blade during the first mode of transverse vibration. In this analysis, the numerical models without defects and also with V-notches were defined. The quality of the numerical solution was checked by the convergence analysis. Obtained results were next used as an input data into crack initiation (ε–N) analyzes performed for the load time history equivalent to one cycle of the transverse vibration. In the fatigue analysis the different methods such as: Neuber elastic–plastic strain correction, linear damage summation and Palmgreen–Miner rule were utilized. As a result of ε–N analysis, the number of load cycles to the first fatigue crack appearing in the compressor blades was obtained. Moreover, the influence of the blade vibration amplitude on the number of cycles to the crack initiation was analyzed. Values of the fatigue properties of the blade material according to Baumel–Seeger and Muralidharan methods were calculated. The influence of both the notch radius and values of the UTS of the blade material on the fatigue behavior of the structure was also considered. In the last part of work, the finite element results were compared with the results of an experimental vibration HCF tests performed for the compressor blades.