Development of the Euro fracture toughness dataset

Ten European laboratories have generated the Euro fracture toughness dataset in order to provide an experimental data base sufficiently large to study specimen size and temperature effects on cleavage fracture toughness in the ductile-to-brittle fracture transition regime. The Euro fracture toughness dataset quantifies the fracture behaviour of the quenched and tempered pressure vessel steel DIN 22NiMoCr37. This material is frequently used in nuclear power plants. About 800 fracture toughness tests were performed using compact tension specimens with a size range from 1/2T to 4T. lower shelf temperature regime, no significant specimen size effects on cleavage fracture toughness scatter was observed. At higher temperatures, the lower tails of the toughness scatter bands are not significantly effected by the specimen size but with decreasing specimen size the toughness scatter increases due to the fact that the upper part of the scatter band is extended. The presence of a specimen size effect on fracture toughness scatter coincides with the appearance of single cleavage initiation sites at the fracture surface. At the lower shelf temperature both, cleavage initiation sites and size effects are not observed whereas at higher test temperatures both phenomena are present. The specimen size effect trends and the corresponding fracture surface morphology support a weakest-link type cleavage fracture mechanism in the ductile-to-brittle transition regime. A unique correlation between the amount of ductile tearing and cleavage fracture toughness was observed for the steel investigated. This result offers the possibility to determine cleavage fracture toughness from post-test fracture surface examinations. the large number of tests and the wide range of testing conditions, the Euro fracture toughness dataset gives a comprehensive insight into specimen size effects and temperature effects on ductile-to-brittle transition fracture. The Euro fracture toughness dataset includes a large set of raw test data such as load versus load line displacement curves and raw tensile test data for deriving stress–strain curves. The Dataset can be downloaded from the internet via the address ftp://ftp.gkss.de/pub/eurodataset.