Fracture mechanics based fretting fatigue life predictions in Ti–6Al–4V

A fracture mechanics based crack propagation analysis is developed to work directly with the output of a contact mechanics stress analysis for fretting fatigue. A series of remote load fatigue tests were conducted on specimens that had previously been subjected to fretting fatigue loading conditions. The growth of these prior fretting induced cracks were monitored and compared to results from the crack propagation analysis. A combined fatigue crack formation and propagation analysis was then applied to other fretting fatigue experiments with good success. The creation of fretting fatigue stress-life curves is also demonstrated.