Loading nature of the interfacial cracks in a joint component under fusion-relevant thermal loads

One of the standard design concepts for divertor components in a fusion reactor is the bonded joint structure. Understanding the loading nature of interfacial cracks are significant for the assessment of structural integrity of divertor joint components. In this paper, the thermomechanical loading nature of interfacial cracks is discussed. A bi-material joint element consisting of the CFC/TZM system is considered. A typical fusion operation condition is simulated assuming a pulsed high heat flux loading. Stress singularities near the interfacial crack tips are characterized quantitatively in terms of the fracture mechanical parameters. The evolution of the stress intensity factors and the energy release rate during the given transient thermal load are determined. The difference in loading characteristics between the edge crack and the center crack is discussed. High heat flux cycling tests are performed on brazed CFC/TZM divertor elements in an electron beam test facility. The microstructures of the damaged interface agree with the predicted fracture modes. The loading nature and possible failure mechanisms are discussed for a fusion-relevant thermal loading.