Corrosion behavior of CLAM steel weldment in flowing liquid Pb-17Li at 480 °C

CLAM (China Low Activation Martensitic) steel is considered as one of the candidate structural materials in liquid LiPb blanket concepts. Welding is one of the essential technologies for its practical application, CLAM steel weldment shows a great difference with base metal due to the effect of welding thermal cycle. In order to investigate the corrosion behavior and mechanism of CLAM weldments in liquid Pb-17Li, the experiments were performed by exposing the TIG weldment samples in flowing LiPb at 480 °C. The weight loss test of exposed specimens show that in 500 h, 1000 h dynamic conditions, corrosion resistance of CLAM steel weldment is poor, SEM analysis shows that the thicker martensite lath in weld area lead to higher corrosion amount, EDS results show that the influence of corrosion on surface elements is small, and surface corrosion is even, EDX analysis shows that the penetration of Pb-17Li does not exist in the joint. With the increasing of exposure time, the corrosion rate decreases. Metallographic analysis shows that the presence of Cr has great influence on the corrosion resistance of the steel matrix. The area short of Cr in thick martensite lath of CLAM steel weldment is easily corroded. After a series of theoretical and experimental analysis, a basic presumably corrosion behavior model is established, which makes contributions to the in-depth understanding of the corrosion mechanism of CLAM weldments.