Sintering of highly porous silica-particle samples: analogues of early Solar-System aggregates

I describe a new method to make particle layers which consist of SiO2 spheres with 0.78 μm radius. The layers were produced by sedimentation of aggregates which had grown in ballistic particle collisions, and the layers had a porosity of 0.95. They were used for experiments on sintering, i.e., the samples were heated in an oven at varying temperatures and heating durations, and the samples were analyzed by scanning electron microscopy. Based on the change of particle diameter, surface diffusion sintering and viscous flow are identified as important transformation mechanisms. The first effect dominated at the start of restructuring and the latter at higher temperatures. The neck growth of adjacent particles was fitted to a surface diffusion sintering model and predicts neck radii as a heating temperature and duration function. Between the temperature range of neck formation and of melting, further restructuring occurred which lead to dissolution of particulate structure and to densification and which resulted in a porous object consisting of straight elongated substructures which connected kinks of higher material density. The thermal transformation is important for the change of strength, collisional behavior, light-scattering properties, and thermal conductivity with relevance to dust aggregates, planetesimals, comets, interplanetary dust particles, and regolith-covered celestial bodies.