Marine environment compatible antireflection coating with nanotop layer on silicon optics

Antireflection coating on silicon optics have crucial importance in thermal device working in 3.6–4.9 μm wavelength region. When the thermal device is used in marine environment, the optics face harsh saline weather condition compared to normal field environment. This deteriorates coated optics and to improve mechanical strength of the coating, a nanotop layer on the antireflection coating has been developed. In this paper a study has been carried out to improve marine environment compatibility by employing a nanolayer on the top of antireflection coating on silicon optics. Optimac synthesis method was used to design the multilayer stack on the substrate with germanium and IR-F625 as high/low refractive index respectively and the layer number was restricted to four layers. The top nanolayer was 60 ± 2 nm thick hafnium dioxide layer developed with ion assisted deposition (End–Hall) on the optics during coating process. The deposition of multilayer coating was carried out inside the coating plant fitted with cryo pump and residual gas analyzer. The evaporation was carried out at high vacuum (2–6 × 10−6 mbar) using electron beam gun and layer thicknesses were measured with crystal monitor. The average transmission achieved was 97% in the spectral band of 3.6–4.9 μm with a hardness of 9.7 GPa on the coated optics.