Effect of Activated Flux on Properties of SS 304 Using TIG Welding
Author/Authors :
Choudhary, S Department of Mechanical Engineering - Ambala College of Engineering, Haryana, Ambala, India , Duhan, R Department of Mechanical Engineering - E-Max College of Engineering,Haryana, Ambala, India
Abstract :
In this experimental work, Manganese oxide (MnO2), Zinc oxide (ZnO), Iron oxide (Fe2O3) and Magnesium chloride (MgCl2) were used as activating flux to investigate the effects for SS 304 in tungsten inert gas (TIG) welding. Ultimate tensile strength, percentage elongation, Penetration depth and width were studied of material SS 304. The experimental results indicated that the MnO2 and Fe2O3 fluxes increases the weld penetration depth and decrease the weld width but ZnO and MgCl2 fluxes shows a little effect on penetration depth and weld depth to width ratio compared with conventional TIG process. Since the activated TIG welding can increase the ultimate tensile strength and percentage elongation.
Farsi abstract :
اين پژوهش مطالعه اي در مورد اكسيد منگنز ، اكسيد روي، اكسيد آهن و كلريد منيزيم كه به عنوان شارهاي فعال استفاده مي شوند را ارائه مي دهد تا اثرات آنها را بر اس اس 304 در جوشكاري گاز بي اثر تنگستن (TIG) بيابد. مقاومت نهايي كششي، درصد ازدياد طول، عمق نفوذ، نسبت عرض و عمق به عرض اس اس 304 مورد مطالعه قرار گرفته است. آزمايش نشان مي دهد كه استفاده از اكسيد منگنز و اكسيد آهن به عنوان شار، عمق نفوذ جوش را افزايش و عرض جوش را كاهش مي دهد. همچنين، استفاده از اكسيد روي و كلريد منيزيم به عنوان شار افزايش كمي در عمق نفوذ و نسبت عرض به عمق جوش در مقايسه با فرايند رايج TIG نشان مي دهد. استحكام كششي نهايي و درصد ازدياد طول در جوشكاري شار فعال TIG افزايش يافته است.
Keywords :
TIG welding , Different Fluxes , Tensile strength , Penetration depth
Journal title :
Astroparticle Physics