Effects of Different Lasers and Particle Abrasion on Surface Characteristics of Zirconia Ceramics

Objective: The aim of this study was to assess the surface of yttrium-stabilized tetragonal zirconia (Y-TZP) after surface treatment with lasers and airborne-particle abrasion. Materials and Methods: First, 77 samples of presintered zirconia blocks measuring 10 × 10 × 2 mm were made, sintered and polished. Then, they were randomly divided into 11 groups (n=7) and received surface treatments namely , Er:YAG laser irradiation with out- put power of 1.5 , 2 and 2.5 W , Nd:YAG laser with output power of 1.5, 2 and 2.5 W, CO2 laser with output power of 3, 4 and 5 W, AL2O3 airborne-particle abrasion (50μ) and no treatment (controls). Following treatment, the parameters of surface roughness such as Ra, Rku and Rsk were evaluated using a digital profilometer and surface examination was done by SEM. Results: According to ANOVA and Tukey’s test, the mean surface roughness (Ra) after Nd:YAG laser irradiation at 2 and 2.5 W was significantly higher than other groups. Roughness increased with increasing output power of Nd:YAG and CO2 lasers. Treated surfaces by Er:YAG laser and air abrasion showed similar surface roughness. SEM micro- graphs showed small microcracks in specimens irradiated with Nd:YAG and CO2 lasers. Conclusion: Nd:YAG laser created a rough surface on the zirconia ceramic with many microcracks; therefore, its use is not recommended. Air abrasion method can be used with Er:YAG laser irradiation for the treatment of zirconia ceramic