EFFECT OF pH ON ELECTROLESS Ni-P COATING OF CONDUCTIVE AND NON-CONDUCTIVE MATERIALS
Author/Authors
Moniruzzaman, M. Bangladesh University of Engineering and Technology - Department of Materials and Metallurgical Engineering, Bangladesh , Roy, Subrata Bangladesh University of Engineering and Technology - Department of Materials and Metallurgical Engineering, Bangladesh
From page
481
To page
489
Abstract
Electroless nickel-phosphorus (Ni-P) coating of carbon steel as well as a polypropylene substrate was conducted using sodium hypophosphite as a reducing agent in alkaline media. The influence of pH on coating appearances and the properties of the coatings for both steel and the polypropylene substrate were studied. A nickel-phosphorus coating of good appearance was obtained in the pH range between 5.5 and 12.5 on the carbon steel substrate and between 8.5 and 12 on the polypropylene substrate. The percentage of Ni content in the coating increased with increasing pH of the bath solution. A smooth, uniform microstructure was found in the coating deposited in relatively lower pH solutions compared to higher pH baths. The microhardness of the Ni-P coating decreased with an increasing percentage Ni content in the deposit.
Keywords
Electroless coating , Nickel , phosphorus , Solution pH , Conditioning.
Journal title
International Journal of Automotive and Mechanical Engineering (IJAME)
Journal title
International Journal of Automotive and Mechanical Engineering (IJAME)
Record number
2561722
Link To Document