Mechanochemical synthesis of alumina nanoparticles

Abstract: Nano- size alumina particles have been synthesized by mechanical activation of a dry powder mixture of AlCl3 and CaO. Mechanical milling of the above raw materials with the conditions adopted in this study resulted in the formation of a mixture consisting of crystalline CaO and amorphous aluminum chlorides phases. There was no sign of chemical reaction occurring during milling stage as evidenced by x-ray diffraction studies. Subsequent heat treatment of the milled powder at 350?C resulted in the occurrence of displacement reaction and the formation of Al2O3 particles within a water soluble CaCl2 matrix. The effect of higher temperature calcinations on the phase development in this powder mixture was followed by X-ray diffraction (XRD) analysis and scanning electron microscope ( SEM). Differential thermal analysis (DTA) was used to compare the thermal behavior between the milled and unmilled powders. Perhaps the most important result in this study was the observation of alpha-Al2O3 phase at a very low temperature of 500C.