Dobbins, Tabbetha Louisiana Tech University - Institute for Micromanufacturing, USA , Dobbins, Tabbetha Grambling State University - Department of Physics, USA , Abrecht, Mike University of Wisconsin at Madison - Synchrotron Radiation Center, USA , Uprety, Youaraj Louisiana Tech University - Institute for Micromanufacturing, USA , Moore, Kristan Grambling State University - Department of Physics, USA
Abstract :
This study reports reaction pathways to form TiAlx metallic complexes during the high energy ball milling of 4 mol% TiCl3 with NaAlH4 powders determined using local structure analysis of Tix+ and Alx+ species. Using x-ray photoemission electron microscopy (XPEEM) and x-ray diffraction (XRD), the oxidation state of Alx+ and Tix+ and the crystalline compounds existing in equilibrium with NaAlH4 were tracked for samples milled for times of 0 (i.e. mixing), 5, and 25 min. XPEEM analysis of the Al K edge after 5 min of milling reveals that Al remains in the 3+ oxidation state (i.e. in NaAlH4) around Ti0-rich regions of the sample. After 25 min of high energy milling, Ti0 has reacted with Al3+ (in nearby NaAlH4) to form TiAlx complexes. This study reports the pathway for TiAlx complex formation during milling of 4 mol% TiCl3 catalyzed NaAlH4 to be as follows: (1) Ti3+ reduces to Ti0 (with Al3+ near Ti0 regions) and (2) Ti0 reacts with Al3+ in NaAlH4 to form TiAlx complexes