Author/Authors :
Jaafar, Juhana Universiti Teknologi Malaysia - Advanced Membrane Technology Research Centre (AMTEC), Malaysia , Ismail, A. F. Universiti Teknologi Malaysia - Advanced Membrane Technology Research Centre (AMTEC), Malaysia , Matsuura, T. University of Ottawa - Department of Chemical Engineering, Industrial Membrane Research Laboratory, Canada , Othman, M. H. D. Universiti Teknologi Malaysia - Advanced Membrane Technology Research Centre (AMTEC), Malaysia , Rahman, Mukhlis A. Universiti Teknologi Malaysia - Advanced Membrane Technology Research Centre (AMTEC), Malaysia , Yusof, N. Universiti Teknologi Malaysia - Advanced Membrane Technology Research Centre (AMTEC), Malaysia , Lau, W. J. Universiti Teknologi Malaysia - Advanced Membrane Technology Research Centre (AMTEC), Malaysia
Abstract :
Sulfonated poly (ether ether ketone) (SPEEK)/Cloisite 15A® nanocomposite membranes were prepared via solution intercalation method. For better dispersion of nanoclay in the polymer matrix, the solution intercalation method was modified and a compatibilizer was introduced. The state of nanoclay dispersion was determined by FESEM. The effect of the solution formulation preparation method and compatibilizer on the performance properties such as proton conductivity and methanol permeability of all membranes was studied. FESEM analysis confirmed that SPEEK/Cloisite 15A® nanocomposite membrane prepared via modified solution intercalation method and in the presence of compatibilizer was the best membrane in terms of its morphological structure. Due to its well nanoclay distribution in polymer matrix, this kind of membrane exhibited the highest selectivity owing to its high proton conductivity and low methanol permeability. SPEEK/Cloisite 15A® with compatibilizer prepared via modified solution intercalation method was found to be the best membrane.
Keywords :
SPEEK , Cloisite 15A® , 2,4,6 , triaminopyrimidine , nanocomposite , DMFC