Growth of CrSi2 Nanostructures Using CrCl2 Powder on Si Substrates
Author/Authors
Li, Wen Shizuoka University - School of Science and Technology, Japan , Erchao, Meng Shizuoka University - School of Science and Technology, Japan , Matsushita, Tomoji Shizuoka University - Faculty of Engineering, Japan , Oda, Shingo Shizuoka University - Faculty of Engineering, Japan , Ishikawa, Daisuke Shizuoka University, - Faculty of Engineering, Japan , Nakane, Kaito Shizuoka University - Faculty of Engineering, Japan , Tatsuoka, Hirokazu Shizuoka University - Faculty of Engineering, Japan
From page
21
To page
24
Abstract
Chromium disilicide (CrSi2) nanostructures were grown by the exposure of Si (111) substrates to CrCl2 vapor in an argon gas flow at atmospheric pressure without using any metal catalyst. Dependence of the growth condition on the structural property was investigated. Hexagonal-shaped CrSi2 microrods were grown at 750 °C with 0.05 g of CrCl2. As the quantity of CrCl2 increased to 0.1 g, the bundle of CrSi2 nanowires with microrods and web-liked CrSi2 nanostructure with turning angles were grown at 750 °C and 700 °C, respectively. The preliminary discussion on the growth mechanism of CrSi2 micro- and nanostructures was carried out.
Keywords
CrSi2 , microrods , nanostructures , thermoelectric material
Journal title
Makara Journal Of Technology
Journal title
Makara Journal Of Technology
Record number
2717579
Link To Document