Simultaneous Measurement of Thermophysical Properties and Dielectric Properties of PZT-Based Ferroelectric Ceramics by Thermal Radiation Calorimetry

Simultaneous measurements of thermophysical properties and dielectric properties have been performed for PZT-based ferroelectric ceramics. An apparatus based on thermal radiation calorimetry was used in the present measurements. Anomalies in the thermophysical properties were observed near the ferroelectricto- paraelectric phase transition temperature. The anomalous peak was at almost the same temperature as the inflection point of the dielectric constant. It was found that modification of PZT with increasing Nb, Mg, Zn, and Sr causes a decrease of the Curie temperature and an increase of the hysteresis phenomena for the phase transition, and the values of the thermal conductivity increase with temperature similar to amorphous materials.