Oxidation Behaviour of Sputtered Ni-3Cr-20Al Alloy

The oxidation behavior of sputtered Ni-3Cr-20AI coating at 900°C in air was investigated. A dense Al2O3 layer was formed on the sputtered Ni-3Cr-20AI coating after 200 h oxidation. However, owing to the segregation of Ni3Al during oxidation process at high temperature, the spinel NiAI2O4 was also formed in the Al2O3 layer. It was found that the formation of NiAl2O4 had no detrimental effect on the oxidation resistance of the sputtered Ni-3Cr-20AI coating due to the excellent adhesion shown by the Al2O3 and NiAl2O4 complex oxide scale.