Deformation behaviour and damage accumulation of cortical bone specimens from the equine tibia under cyclic loading

Despite its clinical importance, the fatigue behaviour of cortical bone has not been examined as widely as its static behaviour. In the present study, specimens from the tibiae of horses have been subjected to load-controlled single step tests. The cyclic deformation behaviour was described by the development of stress–strain hysteresis parameters over the lifetime. The fatigue behaviour of bone is characterised by cyclic softening which is most distinctive towards the end of the lifetime. The microstructural damage accumulated during cyclic loading results in a loss of stiffness, asymmetrical deformation of the bone in tension and compression in cyclic creep. As shown by light and scanning electron microscopy, microcrack formation and growth is the main damage mechanism. The crack growth behaviour is strongly influenced by the microstructure, the stress components and the absolute value of the local stresses. Lower local stresses and/or compressive mean stresses lead to a dominant influence of the shear stress components with shear failure at inner interfaces. With increasing crack length, that is, higher local stress amplitudes, or tensile mean stresses, the microstructure is more and more ignored and failure occurs primarily under the influence of the normal stress components. This can be clearly seen on the fracture and specimen surfaces.