The evaluation of resin composite consistency

The evaluation of resin composite consistency Pages 424-428 Martin J. Tyas, Derek W. Jones, Amin S. Rizkalla Close Preview Purchase PDF (78 K) | Related Articles AbstractAbstract | Figures/TablesFigures/Tables | ReferencesReferences Abstract Objective. To evaluate a method for the assessment of the consistency of unset resin composite. Methods. Fourteen commercial resin composites were selected, which had a range of consistencies as assessed subjectively. The material was placed in a cylindrical mold with 8 mm diameter and 8 mm depth, and a glass rod with 4.37 mm diameter driven into the composite at 24.4 mm min−1 for 6 s, i.e., to a depth of 2.44 mm. The maximum force reached during the 6 s period was recorded, and used as a measure of consistency. Results. Consistency values ranged from 0.33 N to 31.3 N, with the highest values being found for some of the recently introduced ‘packableʹ materials. The reliability of the test was high. Significance. The test may be useful as a standard method of assessing resin composite consistency. Article Outline 1. Introduction 2. Materials and methods 3. Results 4. Discussion 5. Conclusions Acknowledgements References