Dental resin composites containing ceramic whiskers and precured glass ionomer particles

Objectives: Glass ionomer, resin-modified glass ionomer, and compomer materials are susceptible to brittle fracture and are inadequate for use in large stress-bearing posterior restorations. The aim of this study was to use ceramic single crystal whiskers to reinforce composites formulated with precured glass ionomer, and to examine the effects of whisker-to-precured glass ionomer mass ratio on mechanical properties, fluoride release, and polishability of the composites. Methods: Silica particles were fused onto silicon nitride whiskers to facilitate silanization and to improve whisker retention in the matrix. Hardened glass ionomer was ground into a fine powder, mixed with whiskers, and used as fillers for a dental resin. Four control materials were also tested: a glass ionomer, a resin-modified glass ionomer, a compomer, and a hybrid composite. A three-point flexural test was used to measure flexural strength, modulus, and work-of-fracture. A fluoride ion-selective electrode was used to measure fluoride release. Composite surfaces polished simulating clinical procedures were examined by SEM and profilometry. Results: At whisker/(whisker+precured glass ionomer) mass fractions of 1.0 and 0.91, the whisker composite had a flexural strength in MPa (mean (SD); n=6) of (196 (10)) and (150 (16)), respectively, compared to (15 (7)) for glass ionomer, (39 (8)) for resin-modified glass ionomer, (89 (18)) for compomer, and (120 (16)) for hybrid composite. The whisker composite had a cumulative fluoride release of nearly 20% of that of the glass ionomer after 90 days. The whisker composites had surface roughness comparable to the hybrid resin composite. Significance: Composites filled with precured glass ionomer particles and whiskers exhibit moderate fluoride release with improved mechanical properties; the whisker-to-glass ionomer ratio is a key microstructural parameter that controls fluoride release and mechanical properties.