5-Fluorouracil release from copolymeric hydrogels of itaconic acid monoester : I. Acrylamide-co-monomethyl itaconate

The aim of this work was to test the application of new copolymeric poly(acrylamide-co-monomethyl itaconate) (A/MMI) hydrogels to 5-fluorouracil (5-FU) release. Three different compositions of copolymers have been studied, 90A:10MMI, 75A:25MMI and 60A:40MMI. The equilibrium swelling degree in saline solution was between 76 and 80% depending on the copolymer composition. 5-FU, as the sodium salt, was trapped in the gels by including it in the feed mixture of polymerization. The swelling kinetics of the hydrogels in saline solution were studied at four temperatures, and the diffusion coefficient and the activation energy of the process were obtained. The 5-FU release as a function of temperature and disc load was studied; the diffusion coefficient and the activation energy of the release process were also obtained. The diffusion studies follow Fickʹs second law.